Fatigue of commercial aluminium alloys

Abstract

Fatigue crack propagation has been observed for a number of commercial aluminium alloys. Comparable data was obtained for a variety of crack and specimen geometries over a range of crack lengths for a given alloy. Where crack propagation only was of interest the initiation event has been excluded by pre-cracking the specimen using a fin of material adjacent to the crack face. By this method a controlled defect size is introduced in to the specimen. By modification of the D.C. potential drop method it has been shown possible to measure the growth of cracking from 0.12mm by this method. Crack growth from defects greater than 0.6mm have been shown to give conventional crack propagation deduced by principle of similitude. Fatigue fracture surface analysis has been conducted for cracking from both free surfaces and from blunt notches. A `quasi cleavage' feature has been identified and is shown to be prominent when the fatigue stress intensity range is below 10 MNm-3/2.

Divisions: College of Engineering & Physical Sciences > School of Engineering and Technology > Mechanical, Biomedical & Design
Additional Information: Department: Mechanical and Production Engineering If you have discovered material in AURA which is unlawful e.g. breaches copyright, (either yours or that of a third party) or any other law, including but not limited to those relating to patent, trademark, confidentiality, data protection, obscenity, defamation, libel, then please read our Takedown Policy and contact the service immediately.
Institution: Aston University
Uncontrolled Keywords: Fatigue,commercial aluminium alloys
Last Modified: 08 Dec 2023 08:19
Date Deposited: 11 Jan 2011 10:58
Completed Date: 1986
Authors: Hunt, Anthony W.