Semsarilar, Mona, Greenall, Martin J., Balzer, Alex H., Sarkar, Amit Kumar, Gomri, Chaimaa, Benkhaled, Belkacem Tarek, Hohme, Anke-Lisa, Held, Martin, Abetz, Volker, Hutchins-Crawford, Helena J., Maitland, Georgia L., Patel, Anisha, Epps III, Thomas H., Topham, Paul and Derry, Matthew (2025). Exploring Microphase Separation in Semi-Fluorinated Diblock Copolymers: A Combined Experimental and Modelling Investigation. ACS Polymers Au ,
Abstract
We report the combined experimental and theoretical study of the bulk self-assembly behavior of polystyrene-block-poly(2,3,4,5,6-pentafluorostyrene) diblock copolymers. These block copolymers were designed to create highly antagonistic blocks (with a high Flory–Huggins interaction parameter, χ) with minimum disruption to the molecular construct (i.e., only replacing five hydrogen atoms with five fluorine atoms). A large library of diblock copolymers (41 samples) was synthesized by reversible addition–fragmentation chain transfer (RAFT) polymerization to map out a major portion of the phase space. All block copolymers exhibited narrow molecular weight distributions with dispersity (D) values between 1.07 and 1.32, and subsequent thermal annealing revealed phase separation into well-defined nanoscale morphologies depending on their molecular composition, as determined from small-angle X-ray scattering and transmission electron microscopy analyses, with an experimental phase diagram being constructed. The χ value at 25 °C for this block copolymer was estimated to be 0.2 using strong segregation theory, based on trends in phase-separated domain spacing and interfacial width. When applying theoretical approaches, the majority of the domain spacing data trends were captured by a coil–coil diblock copolymer model; however, a better fit to the data for samples with shorter fluorinated blocks was obtained with a rod–coil model, indicating that the chains in these fluorinated blocks likely have a higher inherent stiffness and were thus rod-like. This observation demonstrates that, due to the very high value of χ, a transition from coil–coil to rod–coil behavior can be obtained purely by reducing the length of the stiffer of the two blocks and without varying temperature or the chemical composition of the polymers. This work showcases the presence of strong microphase separation within AB diblock copolymers despite the relatively similar chemical composition of the constituent “A” and “B” units, with a clear transition from rod–coil to coil–coil segregation behavior.
Publication DOI: | https://doi.org/10.1021/acspolymersau.5c00109 |
---|---|
Divisions: | College of Engineering & Physical Sciences College of Engineering & Physical Sciences > School of Infrastructure and Sustainable Engineering > Chemical Engineering & Applied Chemistry Aston University (General) |
Funding Information: | ■ ACKNOWLEDGMENTS M.J.D. thank EPSRC for providing DTP studentships for G.L.M. and A.P. (EPSRC DTP 2020−2021, Aston University, grant ref: EP/T518128/1). M.J.D. and M.S. thank the British Council for support via a Hubert Curien Alliance grant (project num |
Additional Information: | Copyright © 2025 The Authors. Published by American Chemical Society. This publication is licensed under CC-BY 4.0 |
Last Modified: | 15 Oct 2025 07:16 |
Date Deposited: | 14 Oct 2025 13:46 |
Full Text Link: | |
Related URLs: |
https://pubs.ac ... ymersau.5c00109
(Publisher URL) |
PURE Output Type: | Article |
Published Date: | 2025-10-10 |
Published Online Date: | 2025-10-10 |
Accepted Date: | 2025-10-01 |
Authors: |
Semsarilar, Mona
Greenall, Martin J. Balzer, Alex H. Sarkar, Amit Kumar Gomri, Chaimaa Benkhaled, Belkacem Tarek Hohme, Anke-Lisa Held, Martin Abetz, Volker Hutchins-Crawford, Helena J. Maitland, Georgia L. Patel, Anisha Epps III, Thomas H. Topham, Paul ( ![]() Derry, Matthew ( ![]() |