In Situ Compatibilized Blends of PLA/PCL/CAB Melt-Blown Films with High Elongation: Investigation of Miscibility, Morphology, Crystallinity and Modelling

Abstract

Ternary-blended, melt-blown films of polylactide (PLA), polycaprolactone (PCL) and cellulose acetate butyrate (CAB) were prepared from preliminary miscibility data using a rapid screening method and optical ternary phase diagram (presented as clear, translucent, and opaque regions) as a guide for the composition selection. The compositions that provided optically clear regions were selected for melt blending. The ternary (PLA/PCL/CAB) blends were first melt-extruded and then melt-blown to form films and characterized for their tensile properties, tensile fractured-surface morphology, miscibility, crystallinity, molecular weight and chemical structure. The results showed that the tensile elongation at the break (%elongation) of the ternary-blended, melt-blown films (85/5/10, 75/10/15, 60/15/25 of PLA/PCL/CAB) was substantially higher (>350%) than pure PLA (ca. 20%). The range of compositions in which a significant increase in %elongation was observed at 55–85% w/w PLA, 5–20% w/w PCL and 10–25% w/w CAB. Films with high %elongation all showed good interfacial interactions between the dispersed phase (PCL and CAB) and matrix (PLA) in FE-SEM and showed improvements in miscibility (higher intermolecular interaction and mixing) and a decrease in the glass transition temperature, when compared to the low %elongation films. The decrease in M w and M n and the formation of the new NMR peaks ( 1H NMR at 3.68–3.73 ppm and 13C NMR at 58.54 ppm) were observed in only the high %elongation films. These are expected to be in situ compatibilizers that are generated during the melt processing, mostly by chain scission. In addition, mathematical modelling was used to study the optimal ratio and cost-effectiveness of blends with optimised mechanical properties. These ternary-blended, melt-blown films have the potential for use in both packaging and medical devices with excellent mechanical performance as well as inherent economic and environmental capabilities.

Publication DOI: https://doi.org/10.3390/polym15020303
Divisions: College of Engineering & Physical Sciences > School of Infrastructure and Sustainable Engineering > Chemical Engineering & Applied Chemistry
College of Engineering & Physical Sciences > Aston Institute of Materials Research (AIMR)
College of Engineering & Physical Sciences > Aston Institute of Urban Technology and the Environment (ASTUTE)
College of Engineering & Physical Sciences
College of Engineering & Physical Sciences > Energy and Bioproducts Research Institute (EBRI)
College of Engineering & Physical Sciences > Aston Polymer Research Group
College of Engineering & Physical Sciences > Engineering for Health
College of Engineering & Physical Sciences > Aston Advanced Materials
Additional Information: Copyright: © 2023 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/). Funding statement: This work was supported by Thailand Science Research and Innovation (TSRI) (Grant Number FRB660001/0179, Contract Number R2566B004), Global and Frontier Research University (Grant Number R2566C052), Naresuan University and was also supported by the European Union’s Horizon 2020 research and innovation programme under the Marie Sklodowska-Curie grant agreement No 871650 (MEDIPOL).
Uncontrolled Keywords: elongation,blend,poly(lactic acid),compatibilizer,films
Publication ISSN: 2073-4360
Last Modified: 20 Jun 2024 07:21
Date Deposited: 30 Jan 2023 08:59
Full Text Link:
Related URLs: https://www.mdp ... 3-4360/15/2/303 (Publisher URL)
http://www.scop ... tnerID=8YFLogxK (Scopus URL)
PURE Output Type: Article
Published Date: 2023-01-06
Accepted Date: 2023-01-03
Authors: Tuancharoensri, Nantaprapa
Ross, Gareth M.
Kongprayoon, Arisa
Mahasaranon, Sararat
Pratumshat, Supatra
Viyoch, Jarupa
Petrot, Narin
Ruanthong, Wuttipong
Punyodom, Winita
Topham, Paul D. (ORCID Profile 0000-0003-4152-6976)
Tighe, Brian J. (ORCID Profile 0000-0001-9601-8501)
Ross, Sukunya

Download

[img]

Version: Published Version

License: Creative Commons Attribution

| Preview

Export / Share Citation


Statistics

Additional statistics for this record