Photochemical degradation of polystyrene


In this work the oxidative degradation of pure polystyrene, polybutadiene and butadiene-modified polystyrene (normally called high impact polystyrene or HIPS) have been studied using a variety of physical and chemical techniques. The changes in dynamic-mechanical properties occurring during the ultra-violet light accelerated weathering of these polymers were followed by a visco-elastometric technique (Rheovibron) in the solid phase over a wide temperature range. Selective cross-linking of the polybutadiene in high-impact polystyrene caused the depression of the low temperature damping peak (tan d) with a corresponding sharp peak in tan d at ambient temperature accompanied by an integral rise in complex modulus. During the same period of photoxidation, the hydroperoxide concentration and gel content increased rapidly, reaching a maximum before decomposing photolytically with the destruction of unsaturation and with the formation of stable oxidation products. Infra-red spectroscopy showed the formation of carbonyl and hydroxyl groups. a,ß-unsaturated carbonyl was also identified and was formed by decomposition of both allylic hydroperoxide and initial peroxidic gel by ß-scission of the graft between polybutadiene and polystyrene. With further photoxidation a more stable ether gel was formed involving the destruction of the conjugating double bond of a,ß-unsaturated carbonyl. Addition of saturated and unsaturated ketones which are potential sensitisers of photoxidation to high-impact polystyrene and polybutadiene failed to photo-initiate the oxygen absorption of the polymers. A prior thermal oxidative treatment on the other hand eliminated the auto- accelerating stage leading to linear kinetics as the concentration of thermally-produced hydroperoxide approached a maximum. Antioxidants which act by destroying hydroperoxide lengthened the induction period to rapid oxygen absorption, whilst a phenolic antioxidant behaved as a weak photo-activator initially and a retarder later. Prior photolysis of high-impact polystyrene photo-activated the unsaturated component and caused similar changes in dynamic-mechanical properties to those found during photoxidation although at a much lower rate. Polybutadiene behaves as a photo-pro-oxidant for the destruction of polystyrene in high-impact polystyrene.

Publication DOI:
Divisions: College of Engineering & Physical Sciences > School of Infrastructure and Sustainable Engineering > Chemical Engineering & Applied Chemistry
Additional Information: Department: Chemistry If you have discovered material in AURA which is unlawful e.g. breaches copyright, (either theirs or that of a third party) or any other law, including but not limited to those relating to patent, trademark, confidentiality, data protection, obscenity, defamation, libel, then please read our Takedown Policy and contact the service immediately.
Institution: Aston University
Uncontrolled Keywords: Photochemical degradation,polystyrene
Completed Date: 1976-06
Authors: Scott, Ashley