Interaction of liquid copper with sintered iron compacts


Interaction of liquid copper with sintered iron is important in brazing, liquid phase sintering and infiltration. In brazing, the penetration of liquid copper into the pores is to be `avoided', whereas in infiltration processes it is `encouraged', and in liquid phase sintering it should be `controlled' so that optimum mechanical properties are achieved. The main objective of the research is to model the interaction by studying the effect of the process variables on the mechanisms of copper interaction in Fe-Cu and Fe-Cu-C systems. This involves both theoretical and experimental considerations. Dilatometric investigations at 950, 1125 and 1200oC, together with metallographic analyses were carried out to clarify the copper growth phenomenon. It is shown that penetration of liquid copper into the iron grain boundaries is the major cause of dimensional changes. Infiltration profiles revealed that copper penetration between the iron interparticle contact points and along iron grain boundaries is a rapid process. The extent of copper penetration depends on the dihedral angle. Large dihedral angles hinder, and small angles promote copper penetration into the grain boundaries. Dihedral angle analysis shows that the addition of 0.6wt.% graphite reduces the number of zero dihedral angle from 27 to 3o and increases the mean dihedral angle from 9.8 to 41.5o. The dihedral angle was lowest at 1125oC and then increased to higher values as the system approached its equilibrium condition. Elementally mixed (E.M.) Fe-Cu compacts showed a rapid expansion at the copper melting point. However, graphite additions reduced compact growth by increasing the mean dihedral angle. In order to reduce the copper growth phenomenon, iron powder was coated with a thin layer of copper by an immersion coating (I.C.) technique. The dilatometric curves revealed an overall shrinkage in the I.C. compacts compared to their corresponding E.M. compacts. Multiple regression models showed that temperature had the most effect on dimensional changes and density had the most contributing effect upon the copper penetration area in the infiltrated powder metallurgy compacts.

Divisions: College of Engineering & Physical Sciences > School of Engineering and Technology > Mechanical, Biomedical & Design
Additional Information: Department: Mechanical and Production Engineering If you have discovered material in AURA which is unlawful e.g. breaches copyright, (either theirs or that of a third party) or any other law, including but not limited to those relating to patent, trademark, confidentiality, data protection, obscenity, defamation, libel, then please read our Takedown Policy and contact the service immediately.
Institution: Aston University
Uncontrolled Keywords: powder metallurgy,liquid phase sintering,infiltration,braqzing
Last Modified: 08 Dec 2023 08:23
Date Deposited: 11 Jan 2011 11:23
Completed Date: 1989-06
Authors: Parvin, Nader


Export / Share Citation


Additional statistics for this record