The synthesis of novel biodegradable polyesters and copolyesters from anhydrosulfites

N'Goala, Karine L.R. (1996). The synthesis of novel biodegradable polyesters and copolyesters from anhydrosulfites. PHD thesis, Aston University.

Abstract

This thesis was concerned primarily with the synthesis and the ring-opening polymerisation of anhydrosulfites (1,3,2-dioxa-thiolan-4-one-2-oxides), and secondly with the copolymerisation of anhydrosulfites with -caprolactone. The polyesters and copolyesters synthesised are of considerable interest in medical applications and also for use as environmental friendly packaging. A range of anhydrosulfites were prepared according to an established method. Aliphatic anhydrosulfites were obtained with a level of purity satisfactory for polymerisation whereas aromatic anhydrosulfites decomposed during distillation and purification by chromatographic techniques. Aliphatic anhydrosulfites with a substituent, such as methyl, isopropyl, n-butyl and isobutyl were studied by NMR spectroscopy. Analysis of these spectra revealed that the five-membered anhydrosulfite ring was puckered and that when the substituent was bulky, rotations about the alkyl chains were restricted. A wide range of anionic initiators may be used to initiate anhydrosulfites. Lithium alkyls turned out to be more successful than alkali metal alkoxides and amides. The molecular weights were found to depend on the basicity of the initiator, the monomer-to-initiator ratio, the nature of the solvent and the polymerisation temperature. The molecular weight M0 of poly(L-lactic acid) ranged from (0.5 to 6)x104. Highly crystalline and purely isotactic poly(lactic acid) was synthesised from L-lactic acid anhydrosulfite (L-LAAS) whereas DL-LAAS led to an amorphous polymer with randomly distributed D-and L-lactic units. This indicated that this polymerisation was not stereoselective. However, the bulkiness of the substituent in the anhydrosulfites molecule was found to influence the stereoselectivity of the polymerisation, thus polyesters with isobutyl or n-butyl pendant group were preferentially isotactic. Block-copolymers of ε-caprolactone and several anhydrosulfites were successfully produced. Block-copolymers of LAAS with ε-caprolactone were also synthesised, but the incorporation of caprolactone units was rather small. In contrast, random copolymerisation of LAAS and ε-caprolactone led to polymers with blocky structures similar to those obtained in the block-copolymerisation of LAAS with  ε-caprolactone.

Divisions: Engineering & Applied Sciences > Chemical engineering & applied chemistry
Additional Information: Department: Chemical Engineering and Applied Chemistry If you have discovered material in AURA which is unlawful e.g. breaches copyright, (either theirs or that of a third party) or any other law, including but not limited to those relating to patent, trademark, confidentiality, data protection, obscenity, defamation, libel, then please read our Takedown Policy and contact the service immediately.
Institution: Aston University
Uncontrolled Keywords: anhydrosulfite,poly(lactic acid),biodegradable,aliphatic copolyesters,poly(caprolactone)
Completed Date: 1996-04